Process for producing iron-free aluminum nitrate solutions



May 14, 196 8 GERRY ETAL PROCESS FOR PRODUCING IRON-FREE ALUMINUM NITRATE'SOLUTIONS Filed Aug. 17, 1964 2 Sheets-Sheet 1 ALUMINA 1 ORE GRINOING' 40-60% HNO3 MIXING a OIGEsTION IOO-zOO PSI c l40-220C J) D l /-AIIN03)3+REO MUD AIR 7 SEPARATION WATER AMMONIA AI(NO3)3 LIQUORJ RED MUD PURIFICATION vIA --PuRGE OF CRYSTALLIZATION IMPuRITIEs H rA|(NOa)3'9HzO CRYSTALS F\ OENITRATION a OxIOE FORMATION RECOVERY 300500;

HNOz AND OXIDES OF NITROGEN HYDRATED ALUM'NA 9/ CALCINATION CELL-GRADE INVENTORS BY ANTON W. YODIS HAROLD T. GERRY RL K. AMANO United States Patent 3,383,166 PROCESS FOR PRODUCENG IRON-FREE ALUMINUM NITRATE SQLUTKONS Harold T. Gerry, Petershurg, Va, Carl K. Amano,

Denver, Colo., and Anthony W. Yodis, Whippany,

N..l., assignors to Allied Chemical Corporation, New

York, NFL, a corporation of New York Filed Aug. 17, 1964, Ser. No. 390,141 3 Claims. (Cl. 23-102) ABSTRACT OF TEE DTSCLQSURE Process for production of aluminum nitrate solutions having a ratio of A1 0 to Fe O of at least about 2,000 which comprises heating at temperatures above 140 C. iron-contaminated aluminum nitrate solutions containing free A1 0 in the presence of at least about 0.10 part Fe O per part A1 0 for a period sufficient to precipitate substantially all the iron.

This invention relates to a process for the production of cell grade alumina from aluminous substances of varying grades, and more particularly to the production of iron-free aluminum nitrate solutions from iron-containing aluminous ores by a controlled single stage digestion with aqueous nitric acid.

Cell grade alumina, that is, alumina of the high purity required for reduction to aluminum metal in electrolytic cells, has been produced in the past, principally from high grade bauxites containing high proportions of aluminum and low proportions of silica and iron, by digesting with caustic alkalis according to the well known Bayer process.

Such processes are not well adapted to the extraction of alumina from ores containing large percentages of silica and/or iron, and for treatment of such ores, various acid extraction processes have been proposed, including extraction with nitric acid. The nitric acid extraction process as heretofore practiced has produced aluminum nitrate solutions contaminated with high proportions of iron which, unless subjected to further expensive purification steps, produced aluminas containing iron in excess of the minimum permissable quantities specified for cell grade alumina, usually less than about 0.05% iron preferably less than about 0.02% iron as Fe O based on the A1 0 content, or a ratio of A1 0 to Fe O of at least about 2,000.

It is an object of the present invention to provide a process involving a single iron separation step for producing aluminum nitrate solutions of the low iron content required for the production of cell grade alumina, from either high or low grade aluminous ores, particularly from low grade ores such as clays and low grade bauxites.

These and other objects are accomplished according to our invention wherein aluminum nitrate solutions containing at least about 6% of aluminum compounds calculated as A1 0 composed of aluminum nitrate and free A1 0 the latter being present in an amount equal to at least about 1.0 part per 100 parts of A1 0 combined as aluminum nitrate, are heated at temperatures between about 140 C. and about 220 0, preferably between about 160 C. and about 200 C., at autogeneous pressures in the presence of at least about .10 part of Fe O per part of A1 6 based on the total aluminum in the solution calculated as A1 0 for a period sufiicient to precipitate substantially all the iron in the aluminum nitrate solution, and the ratio of alumina to iron oxide in the aluminum nitrate solution is greater than about 2,000, and separating the solid precipitate from the liquid aluminum nitrate solution.

Patented May 14, 1958 The aluminum nitrate solutions treated are obtained by leaching or digestion of the aluminous ore at elevated temperatures with aqueous nitric acid of between about 30% and about 60% concentration, the nitric acid being used in a quantity suificient to provide not more than about 98% of the stoichiometric quantity of nitric acid theoretically necessary to convert all the alumina present in the ore to aluminum nitrate, for a period sufiicient to completely exhaust the nitric acid charged and for a period sufiicient to dissolve enough of the alumina values in the ore to leave no free nitric acid in the solution. The uudissolved residue is then separated from the alumina solution, and alumina and nitric acid values are recovered from the aluminum nitrate solution.

For treating aluminous ores initially containing iron in quantities sufiicient to provide the critical ratio of iron to alumina specified above, the ground ore is leached with nitric acid solution and heated at the digestion temperature for the required period in a single stage, usually complete in from about /2 to about 2 hours. This digeslion dissolves a substantial proportion of alumina as aluminum nitrate, together with some free alumina but surprisingly leaves substantially all the iron in an insoluble form as alpha R2 0 hydrate. The temperature of digestion is critical since we have found that ferric nitrate is unstable in aqueous solution at temperatures above about 140 C. in the presence of substantial proportions of ferric oxide, and forms nitric acid and hydrated ferric oxide which is insoluble, whereas aluminum nitrate in aqueous solution under the same temperature conditions is essentially stable and remains in solution. The silica and other inert oxides remain undissolved.

In leaching aluminous ores as above described, it is necessary to carry out the digestion with a deficiency of nitric acid, i.e., less than the stoichiometric equivalent based on the equation If quantities of nitric acid closely approaching the stoichiometric equivalent or in excess thereof are used, substantial quantities of iron are dissolved and thus contaminate ti 2 aluminum nitrate solution to such an extent that the alumina produced therefrom fails to meet the specifications required for cell grade alumina (less than 0.05% Fe O i.e., a ratio of Al O /Fe O in excess of about 2,000).

After digestion of the aluminum nitrate solution, the slurry is filtered or otherwise treated to remove iron oxide and undissolved silica, resulting in a virtually iron free aluminum nitrate solution.

To produce cell grade alumina, the aluminum nitrate solution is then concentrated, as by evaporation, the aluminum nitrate is crystallized as Al(NO -9H 0, leaving impurities such as sodium, calcium, copper, magnesium and the like in the mother liquor, which is separated from the crystals. The aluminum nitrate crystals are then denitrated to form alumina, A1 0 and to recover nitric acid values, for example by melting the crystals at say, about C. in a melt tank and spraying the melt as a liquid into a fluid bed of alumina which is heated and maintained at about 400 C. The aluminum oxide, in the form of a partially hydrated aluminum oxide is drawn off and is calcined at about 1,000 C. or higher to form cell grade alumina.

The mother liquor from the crystallization step is denitrated in a separate fluid bed of alumina to recover the nitric acid values while the impure alumina is discarded.

The off gas streams from the above two denitration operations, containing HNGg, oxides of nitrogen and steam are combined, and fed into a nitric acid scrubbing tower to recover the nitric acid as an aqueous solution of the desired concentration which is recycled to the digestion system.

In treating aluminous ores containing insufiicient iron to provide at least the minimum proportion of Fe O to A1 necessary for effective removal of iron from solution, it is necessary to supply the deficiency of iron oxide before digesting at the critical temperatures indicated. Thus, according to one modification of our invention, there is added to the ground, low iron content ore, a quantity of iron oxide material sufficient to provide at least about .10 part Fe O per part of aluminum, calculated as A1 0 in the resulting mixture, and the resulting mixture is digested with nitric acid at the indicated temperatures as described above. While this procedure may be used with any of the commonly available low iron content ores it is most advantageously employed when treating ores which are relatively low in silica such as, for example high grade bauxite which often contains no more than about 2 to 3% silica.

However, for treating low iron content ores which are high in silica, such as for example, Georgia kaolin clay, which typically analyzes 36.6% A1 0 0.85 Fe O and 40% silica, a preliminary leaching step is preferably carried out to remove the silica prior to the critical digestion step. In carrying out this step, the ground ore is preferably calcined, and is then leached with aqueous nitric acid of the indicated concentration and ratio of total nitric acid to alumina content of the ore, at temperatures of about 90 C. or above preferably between about 90 C. and about 120 C., and atmospheric pressure. Higher temperatures may be used but are not necessary for adequate solution of alumina. This treatment dissolves both aluminum and iron. The resulting slurry is filtered or otherwise treated to separate undissolved residue, mostly undissolved silica.

To the above solution, which contains aluminum and iron nitrates, is added a quantity of acid soluble iron oxide material sufficient to provide at least about .10 part Fe O per part of aluminum calculated as A1 0 in the resulting mixture. The iron oxide material may be added to the solution as above or to the original ore as previouly indicated and may be supplied from any desired source for example, (a) iron bearing residue resulting from the nitric acid autoclave leaching of high iron bauxite, or (b) an iron compound produced by the thermal decomposition of iron nitrate, or (c) addition of an aluminous ore high in iron such as Jamaica bauxite. If the free A1 0 in the solution at this point is below that required to react with all the nitric acid to be liberated by the decomposition of ferric nitrate in the digestion step, a quantity of A1 0 is added, sufficient to provide at least a slight excess of free alumina after exhaustion of the nitric acid so produced.

The resulting iron oxide-containing aluminum nitrateiron nitrate solution, is then digested at temperatures between about 140 C. and about 220 C. under autogeneous pressure until the alumina to Fe O ratio in the solution is greater than about 2,000. Under the indicated temperature conditions and ratios of Fe O to A1 0 in the above mixture, the iron existing in solution as iron nitrate is precipitated, together with the added Fe O as alpha F6203 hydrate and is separated by filtration or other mechanical means. The separated iron oxide residue can be recycled if desired to a new batch of leach filtrate from the clay.

The weight ratio of Fe O to A1 0 in the digestion slurry is critical and iron oxide should be present in an amount of at least about 0.10 part by weight of Fe O per part of A1 0 in order to obtain adequate iron removal. Ratios as high as 1.5 to 1 or higher are operative; however, ratios of Fe O /Al O between about 0.2 and about 0.5 are preferred.

The process of our invention is adapted to continuous or batch-wise operation, and for use with high or low grade bauxite ores and with many clays, particularly the kaolins. In order to provide an economic recovery of alumina, such ores should preferably contain at least about 6% alumina, and will usually have alumina contents ranging from about 30% to about 60%. In order to effect substantially complete iron elimination, the initial iron content should :be high enough to provide at least about 0.10 part of Fe O per part of alumina or should be supplemented with additional Fe O to provide at least this amount. Silica content is not critical and our process is amenable to operation with high or low silica ores. The silica content of such ores will usually range between about 1% and about 20% for the bauxites and up to 40% or higher for the clays. In addition to the main constituents alumina, iron and silica, most aluminous ores contain smaller proportions of other impurities such as various metallic oxides inert to nitric acid and small proportions of alkali and alkaline earth metal compounds, for example, compounds of titanium, calcium, chromium, copper, nickel, sodium, manganese and magnesium. These impurities are also eliminated by our process.

Typical analyses of a number of clays and bauxites suitable for use in our process are shown below.

TYPICAL ANALYSIS OF SUITABLE ORES Percent Typo Ore M 0 F0 0 SiO Spanish Bauxite 49. 6 21.0 0. 2 Portland Hills, Oregon Bat 8S. 6 34. 4 1.26 Salem Hills, Oregon Bauxite. 37.05 21. 5 9. 7 Jamaican Bauxite i 4t). 4 20.2 0.85 High Grade Bauxite 61. 0 0. l4 2. 0 Kaolin Clay, Georgi. 35. 6 0.85 40. 0 Arkansas Kaolin Clay eined) 9. 7 1 25 30. 1 Arkansas Bauxite Kaolin Iiigh Sil :1 (Calcincd) 4. 3 10 30. 0

In the drawings, FIGURE 1 is a flow sheet showing schematically the several steps in our continuous process for producing cell grade alumina from low grade bauxite. FIGURE 2 illustrates the solubility curves of alumina, A1 0 and iron oxide, Fe O respectively, which dissolve from a bauxite containing 49.4% A1 0 and 20.2% Fe O when digested in 50% concentration of nitric acid at temperatures between C. and C.

In FIGURE 1, A denotes the ore grinding step, B denotes mixing of ground ore with HNO solution, C denotes digestion of the nitric acid-ore slurry at elevated temperatures and pressures, D denotes dilution and separation of the aluminum nitrate solution from the silica and iron impurities, E represents the crystallization step in which the mother liquor containing soluble impurities is discarded, F represents the decomposition of crystals to alumina and nitrogen oxides. G is the final calcination step producing cell grade alumina; H and J represent recovered nitric acid and fresh make-up nitric acid respectively used to produce the required concentration of nitric acid for preparing the digestion slurry.

In FIGURE 2, curve 2A depicts the increasing concentration of dissolved AI O with rising temperature upon digestion with 50% nitric acid solution between 100 C. and 170 C. of a bauxite ore initially containing about 50% A3 0 and 20% R2 0 Curve 2B shows the decrease in concentration of soluble FCgOs with increasing temperature.

In carrying out the process according to our invention, aluminous ores are ground, preferably to a fineness such that at least about 75% passes a 200 mesh (Tyler) screen, for example, to 80 mesh (Tyler), and if desired, calcined by heating at elevated temperatures. In some ores, notably the clays, the alumina contents are rendered more soluble by a calcination treatment, others appear to bcncfit less from calcination. The ground ores are mixed with aqueous nitric acid solution of at least about 30% concentration, preferably between about 40% and about 60% concentration, in a quantity which supplies an amount of nitric acid less than that stoichiometrically equivalent to the alumina in the ore based on the equation set forth above, preferably between about 50% and about 90% e.g., between about 3 moles and about 5.4 moles of HNO per mole of A1 Smaller proportions of nitric acid result in interior extractions of alumina from the ore, higher proportions promote greater solubility of the iron components of the ore and prevent production of a purified aluminum nitrate capable of providing alumina cell grade quality.

The nitric acid-ore slurry is then heated to convert the aluminum in the ore to aluminum nitrate and dissolved free A1 0 and digested in single or multiple stages at temperatures above about 140 C. preferably between 160 C. and about 220 C. under autogeneous pressure, usually about 80 p.s.i.g. to 250 p.s.i.g. for a period sulficient to completely exhaust the nitric acid in the mixture, leaving a solution comprising aluminum nitrate and an appreciable proportion of free A1 0 dissolved in the aluminum nitrate solution. As brought out above, the temperatures are critical for effecting iron removal in a single separation step since we have found that ferric nitrate is unstable in aqueous solution at temperatures above about 140 C., in the presence of ferric oxide and forms nitric acid and hydrated alpha ferric oxide of which the latter is insoluble in the solution. On the other hand, aluminum nitrate in aqueous solution under the same conditions is essentially stable and remains in solution. These relationships are shown graphically in FIGURE 2 of the drawings. Temperatures higher than about 220 C. are preferably avoided as they produce higher vapor pressures and produce higher rates of corrosion than do lower temperatures.

Digestion is continued until no free nitric acid remains in the solution, usually a period between about 15 minutes and about 2 hours residence time at the critical digestion temperature, the time depending somewhat on the temperatures used. Besides dissolving the major proportion of alumina in the ore, the digestion step dissolves substantially all of the alkali and alkaline earth metal compounds as the nitrates. If these impurities are unusually high, it may be desirable to add sufficient additional nitric acid to compensate for its loss in converting these compounds to their nitrates. The amount of nitric acid used, however, should in all cases be less than that theoretically necessary to convert all the alumina to aluminum nitrate after correction for loss due to solution of the alkali and alkaline earth metal compounds. Thus, the amount of nitric acid used in such cases will be suiiicient to convert to nitrates, all of the alkali and alkaline earth metal compounds in the ore and in addition, not more than about 98% of the aluminum compounds present.

After completion of the digestion, the solid material is separated from the slurry, after dilution if desired, as by filtration, settling, or centrifugation to remove undissolved silica and precipitated hydrated ferric oxide (red mud). Metallic oxides inert to nitric acid such as titanium dioxide and the like are also removed at this stage.

The resulting aluminum nitrate solution is virtually iron-free, containing less than about the maximum 0.05% iron permitted for cell grade alumina, '.e., a ratio of A1 0 to Fe O greater than 2,000.

In the process of our invention, the simple digestion step serves concomitantly as a means for eliminating iron from high iron content ores and from iron-contaminated aluminum nitrate solutions with no subsequent iron removal steps which have always been necessary in prior art nitric acid processes.

After separation of the purified iron-free aluminum nitrate solution, alumina is recovered therefrom. Preferably the aluminum nitrate solution is concentrated as by evaporation to crystallizing strength preferably to between about 1 1% and about 12% A1 0 content, and then crystallized as Al(NO -9H O and separated from the mother liquor leaving additional impurities, particularly the alkali and alkaline earth metal compounds such as sodium, calcium, magnesium compounds and also other metallic compounds in the mother liquor. The aluminum nitrate crystals are then denitrated to form alumina, A1 0 and to recover nitric acid values. In one method of accomplishing this, the crystals are melted at say, about C. in a melt tank, then sprayed as a liquid into a fluid bed of alumina maintained at about 400 C. The resulting partially hydrated aluminum oxide is continuously drawn off into a receiver and is calcined in a rotary kiln at about 1000 C. to about 1250 C. to form cell grade alumina. The mother liq-uor from the crystallization step is pumped continuously to a second fluid bed of alumina where it is decomposed to liberate nitric acid values. The impure alumina thus produced is discarded. The off gas streams from the two denitration operations are combined, fed to a nitric acid scrubbing tower where nitric acid is recovered at 4060% concentration which is recycled to the digestion system.

The following specific examples further illustrate our invention. Parts are by weight except as otherwise noted.

EXAMPLE 1 A sample of new Spanish bauxite having the following analysis:

Percent A1 0 49.6 Fe O 21,0 Silica 9.2

thus containing about 0.42 part of l e- 0 per part of A1 0 was pulverized so as to pass 73% through a 200 mesh Tyler screen. Then '816 grams of the pulverized bauxite were slurried with 2520 grams of 50% nitric acid, equivalent to 85% of the stoichiometric equivalent of the A1 0 in the sample. The slurry was heated in an autoclave at 170 C. for about '1.5 hours. The slurry was then diluted with 11000 grams of water, cooled to C. and the slurry was filtered thus producing 3222 grams of a clarified aluminum nit-rate liquor assaying 8.71% total Al O 0.00l1% F3 0, and 0.54% free A1 0 The undissolved material was washed and the residue, containing, on a dry basis, 14% A1 0 and 39.6% Fe O was discarded. The filtrate plus the washings (1477 grams containing 4.32% A1 0 and 0.0003% Fe O contained a total of 344.3 grams of A1 0 which represented 85% alumina yield. Ratio of A1 0 to 'Fe O equivalent in the combined filtrate was 8600.

In a run similar in all respects to that described above, but in which the bauxite was calcined at 650 C. for two hours, a filtrate was obtained which contained 91.5% of the A1 0 in the starting ore and a ratio of Al O /Fe O of 6700.

EXAMPLES 2-5 Four samples of bauxite of varying ratio of Fe O to A1 0 were digested with nitric acid as described in Example 1 above except for variations in proportions of nitric acid used in some cases. The bauxites were of the origin and analyses shown in Table I below:

TABLE I.-BAUXITES Analysis. percent Ex. No. Origin AlzO: F020: 5102 F0901] Alzos Portland. Oregon. 33.6 34.4 1. ?6 0.9 Salem. Oregon" 37. 0 21. 5 9.7 0. 58 amaica 40.4 20.2 0.85 0.41 5 "lliL'll Grade 61.0 0.94 2.90 0.015

Sur nam.

After separation of the solid residues obtained in the 7 8 digestions, the respective filtrates had the analyses shown filtrate obtained contained a ratio of A1 O /Fe O of in Table II below: 2200.

TABLE II Example No 2 3 4 5 Percent Stoiohiornetric HNOs used 71 80 85 81 A 80 8.06 0.0 7. 75 1.3 1.00 1.0 1. 30 F0103 0.0013 0. 0014 0. 00073 0.11 AlaOs/FcrOs 4,450 5,700 8, 200 70 It will be noted from the tables that Example 5 wherein EXAMPLE 9 the ratio of Fe O to A1 0 in the original ore was only To 3836 grams of Fe(NO3)3 solution containing an an alllmmun} filtrate i had too low an equivalent of 666 grams Fe O and 1580 grams of HNO alllmma to Oxlde who to provide a cell grade was added 1130 grams calcined Arkansas high silica kaolin clay, containing 44.3% A1 0 2.1% Fe O and EXAMPLE 6 39.0% SiO The amount of A1 0 added in the clay, 500 grams, was such that the equivalent I'INOg content To 3860 grams 9 hquqr resultmgfrom the of the Fe(NO solution was 85% of stoichiometric with autoclave n1tr1c acrd leach1ng of Sunnam baux1te (0.015 h Al O t t f th 1 Th r Fe 0 /Al O as in Example 5, containing 0.11% iron respect to t 9 2 3 con.en 0 e c e e mg 2 3 2 s and having a ratio of A1 0 to Fe O of 61.7, was added i f %i k i i for SIX ii E thben 354 grams of the dry material obtained in Example 1 e we was ana yze W1 few 8 S Own 8' as a residue from the leaching of Spanish bauxite and containing 40% Fe O and 15% A1 0 The resulting Slurry Before Filtrate, slurry was digested under pressure at 170 C. for one Dlgestlonrmmnt Percent hour and was then filtered. The filtrate was analyzed with Total 111201-- 10.05 8.20 results shown below: gjgffg; 3? 8133 Ami/Fem; 0. 725 4, s20 Liquor Before Filtrate, Percent; Digestion Percent It is apparent from the above example that Fe(NO Total A1101 0.3 0.3 liquor can be used to digest alumina bearing ores to gfgf g 3 produce a virtually iron free aluminum nitrate of a purity 1115001 12163... LII: 01. 7 15, 700 capable of producing cell grade alumina. It is apparent from the above example that ironcon- EXAMPLE 10 taminated aluminum nitrate solution can be purified to A bauXite Sample Containing 575% Of alumina and an yield virtually iron free aluminum nitrate of a purity Al O /Fe O ratio of 8/1 (Fe O :Al O of 0.125) was capable of producing cell grade alumina. mixed with a quantity of aqueous nitric acid solu- 40 tion equivalent to 59.3% of the stoichiometric equivalent EXAMPLE 7 of the A1 0 in the bauxite, and the mixture was digested for six hours at 170 C. The slurry was then filtered and 695 grams of Surinam bauxite 0f the composition produced an aluminum nitrate solution having an shown in Example 5 above was mixed with 500 grams of A12O3/Fe2O3 a 583 gggggg sg fi ii ggg z {2 F 35 ratio of 2570 with a yield of 77.2% of the alumina in the mixture containing 41.8% Al O and 17.2% Fe O To Ongmal EXAMPLE 11 the mixture was added 3140 grams of HNO and the mass was heated at 170180 C. for 1.25 hours. The Ground bauxite ore of about 80 mesh, Tyler, conmass was then diluted and filtered and produced a filtrate 50 taining 50% Al O 20% Fe O 9% SiO the balance assaying 0.0026% Fe O equivalent to an Al O /Fe O other impurities, including about 1.5% TiO and subratio f 3200, stantially less than 1% each of sodium, calcium, magnesium, manganese, nickel, copper and chromium com- EXAMPLE 8 pounds, is continuously fed, together with nitric acid 100 grams of Georgia kaolin clay containing 36.6% 55 solution to a premix tank in the ratio of 263 parts by A1 0 0.85% Fe O and 40% SiO were ground to 28 weight of nitric acid solution per part by weight of bauxmesh and calcined at 650 C. for one hour. The calcined ir equivalent to a ratio of 5 mol HNO per mol of clay was then mixed with nitric acid of 50% by weight A1 0 The resulting slurry is continuously fed to a comconcentration, using 85% of the stoichiometric amount of partment digester vessel equipped with agitators wherein acid required to convert all A1 0 in the clay to aluminum 0 the temperature of the mix is raised to 176 C. and mainnitrate, and maintained at 90118 C. under atmospheric tained at this temperature during progression of the slurry pressure for /2 hour. The mass was then diluted and through the digester during a residence time of about 2.5 filtered. Analysis of the filtrate showed that 86.1% Of hours. The digested slurry, 110w containing no free nitric the A1 0 and 31.5% F6203 W re extract d fr m the clay- -acid and containing about 48.9% aluminum nitrate and The weight ratio of Al O /Fe O in filtrate was 131. A 2% free A1 0 in solution, 5.5% Fe O and 3.3% Si0 in 75 m1. sample of the above filtrate containing 86.2 suspension, the balance water, small proportions of other gm./liter combined A1 0 0.85 g./l. free A1 0 and 0.65 water-soluble nitrates and inert solid impurities, is fed to g-/l. F620 was mixed with 2.25 gm. of iron oxide prea dilution tank, diluted and cooled with 52 C. water or pared by decomposing C. P. Fe(NO -9H O to Fe O by preferably with wash water from the subsequent washing heating to 400 C. to form a mixture containing of the filtered or decanted solid mud, dilution being in the ratio of about 1 part dilution water to 1 part of slurry Al O /Fe O by weight. The diluted slurry is then fed to a classifier or thickener where the aluminum nitrate solution is settled ratio of 2.8 and the mixture was autoclaved at 200 C. and separated by a Dorr thickener, from the insoluble for 15 minutes. The resulting mixture was filtered and the solids (red mud), containing undissolved silica, iron and other solid impurities. The solid material from the thickener is reslurried and settled one or more times to recover the entrained soluble alumina values in the red mud, and the wash water used in the dilution of slurry from the digester.

The liquid filtrate from the thickener, containing about 33.3% aluminum nitrate, is concentrated to about 47.5% aluminum nitrate and is crystallized to Al'(NO 9H O in a two stage vacuum crystallizer. The resulting pure crystals (90% of the original feed) are remelted and fed to a denitration stage. The mother liquid (10% of original feed) is in part recycled and in part bled 011 and denitrated separately and the residue is discarded thus eliminating substantially all impurities not removed with the digest mud.

The Al(NO -9H O melt is decomposed by spraying it on a bed of partially hydrated alumina particles in a fluid bed reactor, The alumina formed is withdrawn continuously from the denitrators at 600 F. (325 C.) and sent to the calcining operation. The decomposition gas is further processed to recover its heat value as 45 p.s.i.g. steam to drive the crytallization stage and to recover its nitric acid values.

The hot nitric oxide and water vapors from the denitrators are passed to a bubble cap tower from which 60% nitric acid is withdrawn from the bottom and 45 p.s.i.g. steam withdrawn from the top. After use in the crystallizer, the condensate is returned to the tower while the non-condensibles are sent to a second tower to recover the nitric oxides as weak acid. This weak acid is returned to the first tower.

The hot alumina is calcined at 2300 F. (1260 C.) in a rotary kiln. The product alumina is cooled by a fluidized bed cooler and then sent to storage. Analysis shows this product to contain less than 0.02% F203 and to meet all the specifications for cell grade alumina.

In Table III below is shown the percentages of impurities in the aluminum nitrate digest liquor and in the final calcined cell grade alumina product obtained in the above example, based on r100% A1 in comparison with the percentages of the same impurities in the original bauxite.

TABLE IIL-PERCENT IMPURITIES, 100% AlzOa BASIS While the above describes the preferred embodiments of our invention, it will be understood that departures may be made therefrom within the scope of the specification and claims.

We claim:

1. The process for producing substantially iron-free aluminum nitrate solutions having a ratio of A1 0 to Fe O of at least about 2,000 from low grade aluminous ores which comprises continuously digesting an aluminous ore containing between about 6% and about 60% alumina, and iron in a quantity equal to between about 0.10 part and about 1.5 parts Fe 0 per part of A1 0 by weight, the balance being primarily silica, together with minor proportions of other metallic compound impurities, with aqueous nitric acid solution of concentration between about 30% and about 60% at temperatures between about 140 C. and about 220 C. under autogenous pressure, the amount of nitric acid used being between about 50% and about 98% of the amount theoretically required to convert all the alumina in the ore to aluminum nitrate, and continuing the digestion until no free acid remains in the solution, thereby obtaining an aluminum nitrate solution having a ratio of Al O to Fe O of at least about 2,000.

2. A process for producing substantially iron-free aluminum nitrate solutions having a ratio of A1 0 to Fe O of at least about 2,000 from low grade aluminous ores which comprises digesting an aluminous ore containing between about 6% and about 60% alumina, iron and in a quantity equivalent to between about 010 part and about 1.5 parts F3203 per part A1 0 by weight, the balance being primarily silica and other metallic oxides inert to nitric acid, together with small proportions of alkali and alkaline earth metal compounds, with aqueous nitric acid solution of concentration between about 30% and about 60% at temperatures between about 140 C. and about 220 C. under autogenous pressure, the amount of nitric acid used being an amount theoretically sufficient to convert to nitrates all the alkali and alkaline earth metal compounds present and additionally between about 50% and about 98% of the amount theoretically required to convert all the alumina in the ore to aluminum nitrate, continuing the digestion until no free nitric acid remains in the solution, and thereafter removing precipitated silica and iron oxide from the solution thereby obtaining an aluminum nitrate solution having a ratio of A1 0 to Fe O of at least about 2,000.

3. The process for producing substantially iron-free aluminum nitrate solutions having a ratio of Al O to Fe O of at least about 2,000 from low grade aluminous ores, which comprises digesting an aluminous ore containing an alumina content between about 6% and about 60%, and iron in a quantity equivalent to between about 0. 1 part and about 1.5 parts Fe O per part Al O- by weight, the balance being primarily silica and other metallic oxides inert to nitric acid, together with minor proportions of other metallic compound impurities, with aqueous nitric acid of about 30% to about 60% concentration, at temperatures between about 160 C. and about 220 C. under autogenous pressure, the amount of nitric acid used being between about 50% and about of the amount theoretically required to convert all the alumina in the ore to aluminum nitrate, continuing the digestion until no free nitric acid remains in the solution, and thereafter removing precipitated silica and iron oxide from the solution, thereby obtaining an aluminum nitrate solution having a ratio of A1 0 to Fe O of at least about 2,000.

References Cited UNITED STATES PATENTS 1,421,804 7/-1922 'Mejdell 23-102 1,652, 'll9 =l2/ l927 Halvorsen et al. 23142 1,792,410 2/1931 Buchner 23102 X 2,907,633 10/=1959 Seidel et al. 23--102X 3,211,524 /1965 Hyde et al. 23- 141 3,240,561- 3/ 1966 Brown 23--102 X FOREIGN PATENTS 7,951 6/1963 Japan.

OTHER REFERENCES Chem. Ab., vol, 60, p. 3772-b.